Application : Wet Mill
Material : Iron
Dimensions : As per drawings
Hardness : HRC52-65
Impact Value : AK5-15J
Product Name : Ball Mill Lining
OEM: : Yes
MOQ: : 2 Tons
Inspection : UT&MT
Heat Treatment: : Quenching&Tempering
Custom Ni-hard Ball Mill Lining For Dia2.2m Wet Ball Mill Hardness HRC52-65
Custom Ni-hard Ball Mill Lining For Dia2.2m Wet Ball Mill
Quick Details
Ni-hard Discharge End Liners for Φ2.6m Rod Mill
1. Hardness: More than HRC53
2. International Standard: AS 2027-2002/Ni hard 1.
3. Microstructure: Eutectic Carbide + Martensite + Residual Austenite
Description:
Ni-hard Discharge End Liners for Φ2.6m Rod Mill
1. The Ni-hard End liners are used for grinding feldspar.
2. Hardness: More than HRC53.
3. International Standard:GB/T 8263-1999
AS 2027/Ni-Cr1-550
AS 2027/Ni-Cr2-500
AS 2027/Ni-Cr4-500
AS 2027/Ni-Cr4-600
AS 2027/Ni-Cr4-630
ASTM A 532 1-A,B,C,D
ASTM A 532 2-A,B,C,D,E
ASTM A 532 3-A
4. Microstructure: Eutectic Carbide + Martensite + Residual Austenite.
5. Heat treatment : Air quenching and tempering.
6. The liners are cleaned,sandblasted with a nice surface without any obvious visual defects.
7. Better wear performance & better reliability & cost effective in dry grinding process.
Product Details:
Application :Mine mill
Material :Ni-hard Cast Iron
Dimensions :As per drawings
Hardness :More than HRC53
Impact Value :More than 5J
Technical Parameters
Wuxi Orient Anti-wear Engineering Co., Ltd.
Chemical Composition & Mechanical Property of Wear-resistant Castings
Item |
Cr-Mo Alloy Steel I |
Cr-Mo Alloy Steel II |
Cr-Mo Alloy Steel III |
High Cr white iron | High Cr Alloy Steel | High Manganese Steel | Ni-Hard cast iron |
C | 0.30~0.50 | 0.65~0.90 | 0.40~0.90 | 2.40~3.20 | 1.1~2.2 | 0.90~1.30 | 2.40~3.60 |
Si | 0.50~1.20 | ≤0.75 | 0.70~1.20 | 0.60~1.20 | 0.60~1.20 | ≤0.08 | ≤0.80 |
Mn | 0.40~1.20 | 0.50~1.20 | 0.60~1.00 | 0.50~1.00 | 0.50~1.00 | 11.00~18.00 | ≤2.0 |
Cr | 1.70~2.50 | 1.50~2.50 | 4.00~7.00 | 12.00~30.00 | 11.00~30.00 | 1.50~2.50 | 1.5~10 |
S | ≤0.04 | ≤0.06 | ≤0.04 | ≤0.04 | ≤0.04 | ≤0.04 | ≤0.15 |
P | ≤0.04 | ≤0.06 | ≤0.06 | ≤0.06 | ≤0.06 | ≤0.06 | ≤0.15 |
Mo | ≤0.5 | ≤0.5 | ≤0.5 | 0.10~3.0 | 0.10~3.0 | ≤1.0 | ≤0.10 |
Cu | 0.10~0.60 | ≤0.25 | 0.20~0.40 | 0.10~1.00 | 0.10~1.00 | - | - |
Ni | ≤0.50 | ≤0.30 | 0~0.30 | 0~0.30 | 0~0.30 | - | 3.3~10 |
Re | ≤0.02 | ≤0.02 | ≤0.02 | - | - | - | - |
Equivalent Specifications |
DL/T 681-1999
GB/T26651-2011 |
AS 2074 L2B Mod | DL/T 681-1999 |
GB/T 8263-1999 AS 2027 Cr27 AS 2027 CrMo 15/3 AS 2027 CrMo 20/2/1 ASTM A532 Class III type A 25% Cr ASTM A532Class II type B 15% Cr-Mo BS 4844 3E DIN1695 NFA32401. |
GB/T 5680-1998 DL/T 681-1999 JIS G 5153-1999 ASTM A 128 DIN GX120Mn12 AFNOR:Z120Mn12 |
GB/T 8263-1999 AS 2027/Ni-Cr1-550 AS 2027/Ni-Cr2-500 AS 2027/Ni-Cr4-500 AS 2027/Ni-Cr4-600 AS 2027/Ni-Cr4-630 ASTM A 532 1-A,B,C,D ASTM A 532 2-A,B,C,D,E ASTM A 532 3-A |
|
Material Type | Martensite Steel |
Martensite or Pearlitic Cr Mo Steel |
Martensite Steel | Martensite matrix | Austenitic Mn Steel | - | |
Hardness | HRc≥48 |
HB470 & HB 321~370 |
HRc≥50 | HRc≥56 | HB≤300 | HRc≥56 | |
Impact Value | Ak≥40J | - | Ak≥10J | Ak≥4J | Ak≥80J | - |